Glaçage idiot
1. Caractéristiques des défauts de glaçure
After the sanitary ceramics products are fired in the kiln, the places where the products are connected with the products, ceiling boards, roof supports, etc. are bonded together because of the glaze, which damages one of them.
2. The place where the glaze defect occurs
The foot, water tank cover, mouth of sanitary ceramic products and the place where jacking is required.
3. Causes of Crazy Glaze Defects
(1) After the body is glazed, the glaze at the place where no glaze is needed is not completely cleaned (such as the bottom).
(2) Forgot to rub aluminum oxide on the water tank cover when applying glaze.
(3) During glaze application, the aluminum oxide at the water tank cover mouth was not smeared properly, and there was glaze at the water tank mouth, resulting in glazed products after burning.
(4) The concentration of the aluminum oxide slurry used for coating aluminum oxide during glaze application is improper. Too small concentration will lead to precipitation of the aluminum oxide slurry and uneven composition, which will lead to the loss of the refractoriness and lead to glaze failure.
4. Solution
(1) After glazing, the surface of the body that does not need to be glazed shall be thoroughly wiped clean.
(2) When applying the glaze, the water tank mouth shall be smeared with aluminum oxide according to the process requirements. For example, 1-2 cm of residual glaze shall be left at the two corners of the front of the water tank mouth to prevent the product from being exposed.
(3) The aluminum oxide slurry used for rubbing aluminum oxide shall ensure a certain concentration, and the residual glaze at the base of the glaze body shall be cleaned timely after the rubbing.
Uneven glaze, thin glaze
1. Characteristics of uneven glaze and defects of thick and thin glaze
After the sanitary ceramics are fired in the kiln, the glaze surface of the product is uneven and has different thickness, and the glaze surface presents obvious wavy or fish scale shape.
2. Parts where uneven glaze and thick and thin glaze defects occur
Each part of sanitary ceramics is easy to produce, but its plane position is obvious.
3. Reasons for uneven glaze and thick and thin glaze defects:
(1) The muzzle of the spray gun used during glaze application is too close to the body, and serious ripples appear on the surface of the body after glaze spraying.
(2) The atomization effect of the spray gun used during glaze application is not good (the air pressure is not enough or the amount of glaze spraying is too large), resulting in the thin glaze layer of the glaze body after glaze application.
(3) When glaze is applied, the glaze slurry that has exceeded the shelf life (i.e., metamorphic glaze slurry) is used, which results in obvious glaze flow, glaze accumulation and glaze dripping on the surface of the glaze body when glaze is applied to the surface of the body.
(4) Après l'application de la glaçure, l'opération d'impression de la glaçure sur le corps de la glaçure est incorrecte et une éponge est utilisée pour imprimer correctement la glaçure lorsqu'il n'y a pas de glaçure fluide ou de glaçure accumulée sur le corps de la glaçure.
4. Solution
(1) Lors de l'application de la glaçure, la distance et l'angle entre la buse du pistolet pulvérisateur et le corps doivent être ajustés pour garantir que la surface du corps de la glaçure après l'application de la glaçure est lisse sans ondulations évidentes.
(2) Avant l'application de la glaçure, ajustez l'équipement pour vous assurer que la pression d'air est suffisante, que la quantité de glaçure pulvérisée par le pistolet pulvérisateur est appropriée, que la vitesse du pistolet est uniforme et que l'épaisseur de la glaçure pulvérisée est uniforme.
(3) Il est strictement interdit d'utiliser une pâte de glaçure dont la durée de vie est dépassée. Si la pâte de glaçure s'avère détériorée, elle doit être renvoyée au service de production de pâte de glaçure pour la première fois et une nouvelle pâte de glaçure doit être ajoutée pour l'application de la glaçure.
(4) Lors de l'impression de glaçure sur le corps de glaçure après l'application de la glaçure, une éponge doit être utilisée pour absorber la glaçure résiduelle plutôt que d'appliquer la glaçure lorsqu'il s'agit de glaçure fluide, de glaçure dégoulinante et de glaçure accumulée sur le corps de glaçure.
Le processus de vernissage est un processus majeur dans la production de céramique sanitaire. Une mauvaise utilisation affectera d'abord la qualité du corps de vernis, puis la qualité des produits cuits. Par conséquent, la manière de contrôler les problèmes techniques dans le processus de vernissage est ce que les usines de céramique sanitaire doivent prendre en compte.